Surfacing

Hardsteel 36Mo

Flux-cored wire for automatic and semi-automatic submerged-arc hardfacing of carbon or low-alloy steel parts exposed to metal-to-metal friction at normal and increased temperatures.

Order form

Additional Information

Diameter, mm	3.0 - 4.0
Curent type / Shielding	DC+ / Flux
Working conditions	Metal-to-metal friction at normal and increased temperatures.
Applications	Hardfacing of tracked vehicle undercarriage wheels and rollers, rubber mixer chambers and augers, steel crankshafts, universal joint spiders, etc.

Recommended flux	EFA-1, AN-60, AN-348A
Slag separation	good
Deposit factor, g/A·h	10 - 15
Crack susceptibility	low
Wire consumption, kg	1.05 - 1.2
Hardness of weld metal	HRC 30 - 42

OPERATING CONDITIONS (submerged arc)

Wire diameter, mm	Current, A	Voltage, V	Deposition rate, m/h
3.0	250 – 360	30 – 32	18 – 23
3.2	300 – 400	30 – 32	20 – 25
3.6	340 – 450	30 – 33	20 – 25
4.0	390 – 470	30 – 34	22 – 27

Download

Similar products

PP-Np-25H5FMS

Flux-cored wire for submerged-arc or gas-shielded hardfacing of parts exposed to cyclic thermal load and severe wear.

PP-Np-45

Flux-cored wire for automatic and semi-automatic gas-shielded hardfacing of parts exposed to increased temperatures and substantial relative pressure.

PP-AN163

Flux-cored wire for automatic and semi-automatic open-arc, submerged-arc or gas-shielded hardfacing of parts exposed to cyclic loads, corrosion, cavitation erosion, and metal-to-metal friction.

Hardsteel 38

Flux-cored wire for automatic and semi-automatic submerged-arc hardfacing of parts exposed to metal-to-metal friction at normal and increased temperatures.

PP-Np-20H

Flux-cored wire for submerged-arc, open arc, or gas-shielded hardfacing of parts exposed to metal-to-metal friction, heating up to 450°C, and chemically active environment.

Трансрейл 48

Flux-cored wire for automatic and semi-automatic open-arc hardfacing of parts exposed to metal-to-metal friction and abrasive wear.

Hardsteel 36Mo

Current, A

Voltage, V