PP-Np-200H15S1GRT (PP-AN125)

Flux-cored wire for open-arc hardfacing of parts exposed to abrasive wear.

Order form 
Additional Information
Diameter, mm 1.6 - 4.0
Curent type / Shielding DC+ / Open arc
Working conditions Abrasive wear
Applications

Hardfacing of excavator bucket teeth, lips and walls, grizzly bars, grader and bulldozer blades, grousers, tracked vehicle undercarriage links and sprockets, etc.
Weld formation good
Slag separation almost no slag
Deposit factor, g/A·h 12 - 16
Crack susceptibility  increased
Wire consumption per, kg 1.1 - 1.2
Hardness (3-layer deposit on mild steel) HRC 46 - 58

OPERATING CONDITIONS

Wire diameter, mm

Current, A

Voltage, V

Deposition rate, m/h

Wire stick-out, mm

1.6

160 – 220

24 – 26

10 – 14

30 – 40

2.0

180 – 250

25 – 27

12 – 17

30 – 40

2.4

200 – 290

26 – 28

15 – 19

30 – 40

2.8

260 – 340

26 – 28

18 – 22

30 – 40
Similar products
PP-Np-30H20
Flux-cored wire for submerged-arc, open arc or gas-shielded hardfacing of parts exposed to cyclic loads, corrosion, cavitation erosion, and metal-to-metal friction.
more 
PP-Np-30H4G2M (PP-AN128)
Flux-cored wire for open-arc and submerged-arc hardfacing of parts exposed to metal-to-metal friction with extra alternating and impact loads.
more 
PP-Np-30H
Flux-cored wire for open-arc, submerged-arc or gas-shielded hardfacing of parts exposed to severe abrasive wear and corrosion along with moderate loads at normal or increased temperatures (up to 450°C).
more 
Hardsteel 45
Flux-cored wire for automatic and semi-automatic open-arc, submerged-arc or gas-shielded hardfacing of steel mill rolls exposed to metal-to-metal friction, cyclic thermal load and corrosion.
more 
Hardsteel 36
Flux-cored wire for automatic and semi-automatic submerged-arc or gas-shielded hardfacing of carbon or low-alloy steel parts exposed to metal-to-metal friction at normal and increased temperatures.
more 
Hardsteel 59A
Flux-cored wire for automatic and semi-automatic gas-shielded hardfacing of chromium carbide-hardened martensitic steel pad on the surface of parts exposed to severe abrasive wear and relatively high impact loads.
more