Surfacing

PP-Np-80H20R3T (PP-AN170)

Flux-cored wire for open-arc hardfacing of steel parts exposed to abrasive wear.

Order form

Additional Information

Diameter, mm	3.2
Curent type / Shielding	DC+ / Open arc
Working conditions	Abrasive wear
Applications	Hardfacing of excavator bucket teeth, lips and walls, grizzly bars, grader and bulldozer blades, grousers, sludge pumps, etc..

Weld formation	good
Slag separation	almost no slag
Deposit factor, g/A·h	10 - 15
Crack susceptibility	increased
Wire consumption, kg	1.1 - 1.2
Hardness (3-layer deposit on mild steel)	HRC 58 - 67

OPERATING CONDITIONS

Wire diameter, mm

Current, A

Voltage, V

Deposition rate, m/h

Wire stick-out, mm

3.2

400 – 420

30 – 32

20 – 25

30 – 40

Download

Similar products

PP-Np-18H1G1M (PP-AN120)

Flux-cored wire for automatic and semi-automatic submerged-arc or gas-shielded hardfacing of carbon steel parts exposed to metal-to-metal friction and abrasive wear.

PP-Np-14GST ( 14MnSiTi )

Self-shielding flux-cored wire is designed for hardfacing of parts made of carbon structural steel, exposed to metal-to-metal friction.

PP-Np-200H15S1GRT (PP-AN125)

Flux-cored wire for open-arc hardfacing of parts exposed to abrasive wear.

Hardsteel 59A

Flux-cored wire for automatic and semi-automatic gas-shielded hardfacing of chromium carbide-hardened martensitic steel pad on the surface of parts exposed to severe abrasive wear and relatively high impact loads.

PP-Np-100H

Flux-cored wire for automatic and semi-automatic open-arc or gas-shielded hardfacing of parts exposed to high impact loads and severe abrasive wear at normal or sub-zero temperatures.

Hardsteel 36

Flux-cored wire for automatic and semi-automatic submerged-arc or gas-shielded hardfacing of carbon or low-alloy steel parts exposed to metal-to-metal friction at normal and increased temperatures.