Surfacing

Hardsteel 38

Flux-cored wire for automatic and semi-automatic submerged-arc hardfacing of parts exposed to metal-to-metal friction at normal and increased temperatures.

Order form

Additional Information

Diameter, mm	1.6 - 4.0
Curent type / Shielding	DC+ / Flux
Working conditions	Metal-to-metal friction at normal and increased temperatures.
Applications	Hardfacing of crane wheels, support rollers, brake pulleys, slide guides, road wheels and idlers of tracked vehicles, gear teeth, roller table rollers, shaft seats, etc.

Recommended flux	EFA-1, AN-348A, AN-60, АN-26S/P, АN-20S/P
Slag separation	good
Deposit factor, g/A·h	10 - 15
Crack susceptibility	moderate
Wire consumption, kg	1.05 - 1.2
Hardness of weld metal	HB 320 - 420

OPERATING CONDITIONS

Wire diameter, mm	Current, A	Voltage, V	Deposition rate, m/h
1.6	140 – 220	25 – 29	10 – 15
2.0	160 – 260	25 – 30	12 – 18
2.8	240 – 360	28 – 32	18 – 23
3.2	280 – 420	30 – 33	20 – 25

Download

Similar products

PP-Np-12H ( Np-12Cr )

Flux-cored wire is designed for open-arc, submerged-arc or gas-shielded hardfacing of parts exposed to an abrasive environment with extra risk of corrosion, at normal and increased temperatures (up to 450°C).

PP-Np-80H20R3T (PP-AN170)

Flux-cored wire for open-arc hardfacing of steel parts exposed to abrasive wear.

PP-Np-15

Hardfacing and repair of damaged parts exposed to heavy contact loads.

PP-AN163M/1

Flux-cored wire for automatic and semi-automatic open-arc or submerged-arc hardfacing of parts exposed to cyclic loads, corrosion, cavitation erosion, and metal-to-metal friction.

Hardsteel 59A

Flux-cored wire for automatic and semi-automatic gas-shielded hardfacing of chromium carbide-hardened martensitic steel pad on the surface of parts exposed to severe abrasive wear and relatively high impact loads.

PP-Np-45

Flux-cored wire for automatic and semi-automatic gas-shielded hardfacing of parts exposed to increased temperatures and substantial relative pressure.

Hardsteel 38

Current, A

Voltage, V