Hardsteel 59A

Flux-cored wire for automatic and semi-automatic gas-shielded hardfacing of chromium carbide-hardened martensitic steel pad on the surface of parts exposed to severe abrasive wear and relatively high impact loads.

Order form

Additional Information

Diameter, mm	1.2 - 1.6
Curent type / Shielding	DC+ / Ar, CO₂,Ar + CO₂
Working conditions	Severe abrasive wear and relatively high impact loads
Applications	Hardfacing of working faces on breaking and mill hammers, agricultural, meat-processing and wood-working tools, etc.

Weld formation	good
Slag separation	good
Deposit factor, g/A·h	15 - 22
Crack susceptibility	moderate
Wire consumption per, kg	1.05 - 1.2
Hardness (3-layer deposit on mild steel)	HRC 56 - 61

OPERATING CONDITIONS (Ar + CO₂)

Wire diameter, mm

Current, A

Voltage, V

Gas flow rate,

L/min.

Deposition rate, m/h

1.2

120 – 300

22 – 30

7 – 16

10 – 15

1.6

140 – 320

23 – 32

7 – 18

10 – 15

Download

Similar products

Hardsteel 54

Flux-cored wire for automatic and semi-automatic open-arc hardfacing of carbon or low-alloy steel parts exposed to metal-to-metal friction, alternating and impact loads at normal and increased temperatures.

PP-Np-18 (PP-Np-18CrMnSi)

Designed for automatic and semi-automatic submerged-arc or gas-shielded hardfacing of carbon steel parts exposed to metal-to-metal friction.

PP-Np-150H

Flux-cored wire for automatic and semi-automatic open-arc or gas-shielded hardfacing of parts exposed to severe gas- and hydro-abrasive wear with extra heavy loads.

PP-AN155M

Flux-cored wire for submerged-arc, open arc or gas-shielded hardfacing of parts operating under harsh thermal and strain conditions with thermal and force cycling, or exposed to metal-to-metal friction.

PP-Np-40H

Flux-cored wire for open-arc, submerged-arc or gas-shielded hardfacing of parts exposed to severe abrasive wear and corrosion at normal or increased temperatures up to 450°C.

PP-Np-10H14T (Np-10Cr14Ti)

Flux-cored wire for automatic and semi-automatic open-arc, submerged-arc or gas-shielded hardfacing of parts exposed to high temperatures, high relative pressures, and a corrosive environment.