Surfacing

PP-Np-180H9

Flux-cored wire for automatic and semi-automatic open-arc hardfacing of parts exposed to severe abrasive wear.

Order form

Additional Information

Diameter, mm	1.2 - 4.0
Curent type / Shielding	DC+ / Open arc
Working conditions	Abrasive wear
Applications	Repair of worn parts in the equipment of mining companies and steel foundries, agricultural and construction machinery, excavators, screw conveyors, etc.

Weld formation	good
Slag separation	good
Deposit factor, g/A·h	15 - 22
Crack susceptibility	low
Wire consumption per, kg	1.1 - 1.2
Hardness (3-layer deposit on mild steel)	HRC 55 - 62

OPERATING CONDITIONS

Wire diameter, mm	Current, A	Voltage, V	Deposition rate, m/h	Wire stick-out, mm
1.6	150 – 230	23 – 27	8 – 15	30 – 40
2.0	180 – 280	24 – 28	10 – 18	30 – 40
2.4	220 – 320	25 – 28	13 – 20	30 – 40
2.8	260 – 380	25 – 29	14 – 22	30 – 40

Download

Similar products

Hardsteel 45

Flux-cored wire for automatic and semi-automatic open-arc, submerged-arc or gas-shielded hardfacing of steel mill rolls exposed to metal-to-metal friction, cyclic thermal load and corrosion.

PP-Np-12H ( Np-12Cr )

Flux-cored wire is designed for open-arc, submerged-arc or gas-shielded hardfacing of parts exposed to an abrasive environment with extra risk of corrosion, at normal and increased temperatures (up to 450°C).

ПП-АН185М/1

Flux cored wire for submerged-arc or open arc hardfacing of medium-carbon high alloy which is resistant to metal-to-metal friction, as well as heat- and temperature-resistant.

PP-AN155M

Flux-cored wire for submerged-arc, open arc or gas-shielded hardfacing of parts operating under harsh thermal and strain conditions with thermal and force cycling, or exposed to metal-to-metal friction.

PP-Np-10H14T (Np-10Cr14Ti)

Flux-cored wire for automatic and semi-automatic open-arc, submerged-arc or gas-shielded hardfacing of parts exposed to high temperatures, high relative pressures, and a corrosive environment.

PP-Np-20H4

Flux-cored wire for open-arc and submerged-arc hardfacing of parts exposed to thermal fatigue and high relative pressure.

PP-Np-180H9

Current, A

Voltage, V